Anti-ozonant
Advantages
– Sunprax is less soluble than paraffin waxes under normal temperature which allows immediate and continuous pro – tection for the rubber surface
– Coating will not break or crack at moderate elongation due to the flexible and closely – packed bloomed layer
– As a non-staining and non-coloring agent, Sunprax can be freely used for white and lightly colored compounds
Storage
– Keep the product at a well-ventilated area
– Store away from heat and moisture
– Keep away from sparks and flames
Shelf life
– 12 months
| Identification | 602N | 652 | 672 | 682H | 710 | Test Method |
| Appearance | White bead | |||||
| Specific Gravity (25℃) | 0.93 ± 0.02 | 0.90 ± 0.05 | 0.93 ± 0.02 | 0.92 ± 0.05 | 0.92 ± 0.03 | ASTM D 1963 |
| Melting Point (℃) | 60.5 ± 2.5 | 65.0 ± 3.0 | 67.5 ± 2.5 | 66.0 ± 3.0 | 69.0 ± 3.0 | ASTM D 87 |
| Heat Loss (%) | Max. 0.2 | ASTM D 2974 | ||||
| Ash (%) | Max. 0.3 | ASTM D 2974 | ||||
| Application | Low temperature | Medium high temperature | Medium high temperature | High temperature | High temperatur | – |
R-Wax
Function
– R-wax is an anti-ozonant for latex application
Advantages
– High quality emulsion type wax
– Stable in hard water, used in wide range of pH
– Helps a cured latex product to release better from mold
– Improves product appearance and anti ozone effect
Storage
– Keep the product at a well
– ventilated area
– Store away from heat and moisture
– Keep away form sparks and flames
Shelf life
– 3 months
| Identification | R-WAX | Test Method |
| Appearance | Yellowish-white emulsion | – |
| Specific Gravity (25°C) | 0.95 ~ 1.00 | ASTM D 1168 |
| pH | 8~11 | ASTM D 1067 |
| Solid contents (%) | 20~40% | ASTM D 2974-2.1 |
| Viscosity (mpa.s) | 15~100 | VT-03 Viscometer |
| Application | Latex processing | – |
| Dosage (phr) | 0.5 ~ 1.5 | – |
DISPER-212
Dispersant
Function
– Disperses filler thoroughly in rubber compounds
Advantages
– Reduces temperature and time during mixing process
– Reduces pre-scorch
– Reduces compound viscosity and allows smoother flow
– Enhances plasticity
Storage
– Keep the product at a well-ventilated area
– Store away from heat and moisture
– Keep away from sparks and flames
Shelf life
– 3 months
| Identification | Disper-212 | Test Method |
| Appearance | Light yellow bead | – |
| Specific Gravity (25°C) | 1.15 ± 0.05 | ASTM D 1963 |
| Softening Point (°C) | 102.5 ± 2.5 | ASTM D 3104 |
| Heat Loss (%) | Max. 10.0 | ASTM D 2974 |
| Ash (%) | Max. 10.0 | ASTM D 2974 |
| Application | Dispersant | – |
SDA-21G
Silica Dispersant
Function
– Disperses silica thoroughly in a rubber compound
– Reduces viscosity of rubber compound
Advantages
– Reduction of compound viscosity enables smoother flow of rubber in a mold
– Reduces scorching risks
– Decreases mixing time and mixing temperature
– Enhances plasticity
Storage
– Keep the product at a well-ventilated area
– Store away from heat and moisture
– Keep away from sparks and flames
Shelf life
– 6 months
| Identification | SDA-21G | Test Method |
| Appearance | Light yellow bead | – |
| Specific Gravity (25°C) | 1.00 ± 0.20 | ASTM D 1963 |
| Softening Point (°C) | 104.00 ± 5.0 | ASTM D 87 |
| Heat Loss (%) | Max. 0.5 | ASTM D 2974 |
| Ash (%) | 14.5 ± 2.0 | ASTM D 2974 |
| Application | Silica dispersant | – |
SDA-260
Silica Dispersant
Function
– Dispersant applied to rubber compound containg silica
Advantages
– Decreases viscosity for better flow of rubber compound
– Applied to soft rubber compound
– Applied to low temperature mixing
Storage
– Avoid direct sunlight and keep in cool place with good ventilation
– Keep away from moisture
– Keep away from heat, fire and sparks
Shelf life
– 6 months
| Identification | SDA-260 | Test Method |
| Iodine Value | 60.0 ~ 80.0 | ASTM D 1959 |
| Zinc Content | 7.0~9.0 | ASTM D 1959 |
| Ash (%) | 18.5~21.5 | ASTM D 5185 |
| Softening Point (°C) | 78.5~91.5 | ASTM D 3104 |
SDA-450K
Silica Dispersant
Function
– Zn-free silica dispersant applied to rubber compound containg high levels of silica
Storage
– Assists higher loading of silica in rubber compound
– Decreases viscosity for better flow
– Shortens mixing period and extruding time
Storage
– Avoid direct sunlight and keep in cool place with good ventilation
– Keep away from moisture
– Keep away from heat, fire and sparks
Shelf life
– 6 months
| Identification | SDA-450K | Test Method |
| Specific Gravity (25°C) | 0.8 ~ 1.2 | ASTM D 1963 |
| Heat Loss (%) | Max. 0.5 | ASTM D 2974 |
| Ash (%) | 5.5 ~ 9.5 | ASTM D 2974 |
| Melting Point (°C) | 58.0~72.0 | ASTM D 87 |
HIMIX-40
Homogenizer
Function
– Himix-40 homogenizes mixture of different rubber compounds with differing polarity
– Himix-40 improves the physical property of the final compound by thorough mixing
Advantages
– Provides excellent solubility to wide range of polymers
– Enhances adhesion among differing rubber compounds
– Enhances resistance to bending, aging and calendering
– Faster cure rate provides cost savings
– Lower viscosity provides energy efficiency by easy mastication
Storage
– Keep the product at a well-ventilated area
– Store away from heat and moisture
– Keep away from sparks and flames
Shelf life
– 6 months
| Identification | HIMIX-40 | Test Method |
| Appearance | Black flake | – |
| Specific Gravity (25°C) | 1.10 ± 0.10 | ASTM D 1963 |
| Softening Point (°C) | 98.0 ± 8.0 | ASTM D 3104 |
| Heat Loss (%) | Max. 1.0 | ASTM D 2974 |
| Ash (%) | Max. 5.0 | ASTM D 2974 |
| Application | Homogenizer | – |
HISTAR
Tackifier
Function
– Histar provides tack property for mixture of different rubber compounds with differing polarity
– Histar provides adhesion between carcass and inner-liner
Advantages
– Compatible with wide range of polymers
– Faster cure rate
– Stable scorch time
– Lowers viscosity for better flow during extrusion
– Tack between natural rubber and IsopreneIsobutene rubber
Storage
– Keep the product at a well-ventilated area
– Store away from heat and moisture
– Keep away from sparks and flames
Shelf life
– 6 months
| Identification | HISTAR | Test Method |
| Appearance | Light brown flake | – |
| Specific Gravity (25°C) | 1.09 ± 0.05 | ASTM D 1963 |
| Softening Point (°C) | 100.0 ± 5.0 | ASTM D 87 |
| Acid Value | Max. 0.3 | ASTM D 1980 |
| Heat Loss (%) | Max. 0.5 | ASTM D 2974 |
| Application | Tackifier | – |
HISTAR-90
Tackifier
Function
– A pplied to rubber compound for better adhesiveness
Advantages
– Assists better mix of different polymers and provides adhesiveness
– Applicable to various types of rubber compounds
– Improves compound extrudability
– Stabilizes scorch time
Storage
– Avoid direct sunlight and keep in cool place with good ventilation
– Keep away from moisture
– Keep away from heat, fire and sparks
Shelf life
– 6 months
| Identification | HISTAR-90 | Test Method |
| Softening Point (°C) | 80.0 ~ 100.0 | ISO 4625 |
| Acid Number (mg KOH/gr) | Max. 80.0 | ASTM D 974 |
| Insol. In Cyclohexane (%) | Max. 0.3 | ASTM D 4934 |